FEATURES ●High C.T.Ivalue (above 600V) ●Process simiar to FR-4 including PTH ●punching process applicable Applications ●Test & measurements equipment,tuner,car electronics, power supply etc |
General Properties |
Test Item | unit | Test Condition | Property Data Standard Value |
Tg | ℃ | DSC TMA | 135 130 |
CTE x-axis y-axis z-axis | ppm/℃ | Ambient to Tg | 20 16 55 |
Flammabilty | - | UL-94 | V-0 |
Insulation Resistance | ohm | C-96/20/65 C-96/20/65+D-2/100 | 1x1012-1x1013 1x1010-1x1011 |
Volume Resistivity | ohm-cm | C-96/20/65 C-96/20/65+C-96/40/90 | 1x1014-1x1015 5x1013-5x1014 |
Surface Resistance | ohm | C-96/20/65 C-96/20/65+C-96/40/90 | 5x1012-5x1014 1x1012-1x1013 |
Are Resistance | min/sec | | 110 |
Dielectric Constant(1MHz) | - | C-96/20/65 C-96/20/65+D-48/50 | 4.3-4.7 4.3-5.0 |
Dissipation Factor(1MHz) | - | C-96/20/65 C-96/20/65+D-48/50 | 0.015-0.020 0.018-0.023 |
Comparative Tracking Index | volt | ICE Method | 200 |
Solder Float(260℃) | sec | A | above 120 |
Peel Strength | Cu.foil | kg/cm | A | 1.5-1.8 |
1oz(0.035mm) |
Flexureal Strength | kgf/mm2 | A | 30-40 |
Water Absorption | % | E-24/50+D-24/23 | 0.10-0.15 |
Specimen Thickness:1.6mm | | | |